Acrylic solvent-borne varnish for decorative protection of mineral surfaces with «wet stone» effect.
Intended to create the protective-decorative coating with «wet stone» effect on brick-, stone-, concrete- and other porous mineral surfaces, as well as for wood and wood-fiber materials inside and outside the buildings.
Recommended for finishing of decorative stone and brick setting on facades and basements of buildings, fences, monuments, different surfaces inside the premises.

Main characteristics of the product

  • Wet stone» effect;
  • For various types of mineral surfaces;
  • Efficient protection against weather impacts;
  • Fills pores, prevents the appearance of salt efflorescence, mold, moss;
  • Stands up considerable temperature differences;
  • Considerably improves the surface’ performance characteristics;
  • Saving consumption.

Application of the product

Varnish is ready for use, mix thoroughly before application.
For firstly-painted surfaces: remove dust and other contaminations, degrease the surface.
For renovation of previously painted surfaces: remove the particles of old flaked coating, clean the surface of dust and dirt. Considerably damaged coatings shall be completely removed.
Apply the varnish with a spray-gun, brush or roller at a temperature from minus 10°C to plus 30°C and relative humidity not exceeding 80%. The temperature of the surface to be painted must be at least 3°C higher than the dew point. The varnish is applied in 2 layers, the first layer is primer, the second layer creates the effect of “wet stone”.
Drying time of each coat – 2 hours.
During the work and afterwards the premises shall be thoroughly ventilated.
Use rubber gloves for hands protection.
Instrument cleaning: dearomatized thinner ТМ Мікs color.
Keep away from fire!


2 hours (film polymerization)


0.65 kg, 2.1 kg


20 – 25 m2/kg, per one-layer coating depending on the surface type

Consumption calculator